Manufacture Polypropylene Pipes and PVC pipes

Краснова А.Н. 1
1Владимирский государственный университет имени А.Г. и Н.Г. Столетовых
 Комментарии
Текст работы размещён без изображений и формул.
Полная версия работы доступна во вкладке "Файлы работы" в формате PDF

Manufacturing of Polypropylene Pipes: Polypropylene Pipes (PP) pipes and PPR pipes are manufactured by extrusion in the same way as PE pipes. Particularly in the case of PP pipes there are several different molecular structures available on the market. In the simplest case the molecular chain is built up of one and the same repeating unit often the same as the monomer shown within the brackets). The polymer is then called homo-polymer.

By improvement of PP-r grades high temperature resistant hot tap water pipes have been introduced recently. They can compete with PEX and PB for many hot water applications, but are easier to process than PEX and safer than PB as far as strength reproducibility is concerned. Furthermore, the PP pipes can be jointed by welding, which is not the case with PEX.

Manufacturing of Polyvinyl Chloride Pipes: Polyvinyl Chloride Pipes (PVC) and PPR pipes can be manufactured with or without plasticizers. Examples of the former are garden hose, floor tiling and household articles. The addition of plasticizers increases material flexibility, but leads to some deterioration in other physical properties. Furthermore, some plasticizers display a tendency to migrate, escaping in the course of time so that the plastics becomes brittle. For these reasons, no pastiches are used in the manufacturer of PVC pipes for water mains and sewers. In this respect, the material is characterized as rigid PVC and this variety is termed PVC-U ( unplasticized PVC) according to ISO.

Distinctions are made in raw materials between emulsion, suspension and bulk resins. Manufacturing processes based on this order of raw materials, ensure, among other things, increased purity and lower water absorption in the PVC material. The most common type is suspension PVC (S-PVC), although emulsion PVC (E-PVC) also exists.

Advantages of the system.

Corrosion resistant

The Random Polypropylene possesses a high level of electrical insulation, which prevent the appearance of corrosive phenomena caused by stray currents.

The low affinity of the system towards acid and alkaline substances makes it compatible with the materials which are used in civil construction on a daily basis (lime and cement), as wee as to the majority of the chemical substances which are sometimes present in water pipes.

Low Thermal Conductivity

Substantially reduces the traditional formation of thermal condensation common in metal pipes.

Reduced Pressure Loss

The pipes and accessories are characterized by low roughness of internal surfaces, avoiding the creation of calcium deposits, reducing pressure loss to the minimum.

Acoustic insulation – low noise

The characteristics of the raw material and the thicknesses used confer high acoustic insulation to the system.

Organoleptic properties

PP-R is an entirely nontoxic product, guaranteeing that the system transport clean water.

Adequate life cycle

According to the clearance curve it is possible to observe that for water installations with defined temperatures and pressures, the system will last more than 50 years.

Reduced installation time

The most relevant characteristics of the PP-R system is the union of all elements through thermal fusion. This method is safe and easy to work with when compared with traditional products.

Recommendations for the appropriate use for the Systems

PP-R, like all thermoplastics, should not be directly exposed to sunlight.

PP-R, material it's crystallizable, stocked not less then +5 °C

PPR, is made of thermoplastic material. High and heavy load shape / reap the disorder is caused. 1 meter higher than the pipe on top of your stocking.

Thermoplastic material is flammable. Do not allow direct contact with fire PPR products!

Please use thermoplastic heaters to give shape.

The pipe must be protected from powerful hitting.

Healthy for the resource, of the ambient temperature is at least +5 °C

Use Teflon tape or liquid to avoid leaks do not use accessories with conical bolts or non-calibrated, and tighten without excessive force.

Pressure test. Test control.

Acc. to the Technical Rules for Potable Water Installations DIN 1988 have to be (while still visible) hydraulically pressure tested all pipelines. The test pressure has to be 1.5 times of the operating pressure. Due to the material properties of SupraTherm pipes a pressurization causes an expansion of the pipe. Different temperatures of pipe and test medium lead to alterations of pressure. A temperature change of 10 K corresponds to a pressure difference of 0.5 to 1 bar.

The pressure test of SupraTherm pipe systems should be made with a constant temperature of the medium. The hydraulic pressure test requires a preliminary, principal and final test. In the preliminary test the system is pressurized with the 1.5 times of the maximum operating pressure. This test pressure has to be re-established twice within 30 minutes within an interval of 10 minutes. After a test time of a further 30 minutes the test pressure must not drop more than 0.6 bar. No leakage may appear.

The preliminary test is to be followed directly by the principal test. Test time is 2 hours. Now the test pressure taken from the preliminary test may not fall more than 0.2 bar. The final test is made with a changing pressure of 1 bar and 10 bars. The pipe system must be unpressurized between each test cycle. Between each test course the pressure has to be released. No leakage must appear at any point of the tested installation system.